Phosphate High Alumina Brick

 Phosphate high alumina bricks are made of high-quality high-alumina bauxite, combined with aluminum dihydrogen phosphate, and dried in an oven.

Characteristics

Phosphate high alumina bricks have high load softening temperature, high compressive strength, good thermal shock stability, wear resistance and peeling resistance. It has the characteristics of stable performance, short construction period, energy saving and environmental protection.

Phosphate High Alumina Brick Specifications

ItemChemical BondedPhosphate Bonded – PPhosphate Bonded – PAHigh RUL
Al2O3 (%)≥75 ≥75 ≥80 ≥78
Fe2O3 (%)≤2≤2≤2≤2
CaO (%)0.60.6
Bulk & Density, g/cm32.652.72.752.8
Refractoriness ( ℃)≥1770≥1790≥1790≥1790
Apparent Porosity (%)≤18≤18-21≤20≤19
Cold Crushing Strength MPa≥60≥70≥75≥80
Refractoriness Under Load of 0.2MPa, ℃≥1400≥1350≥1450≥1460
Thermal Shock Resistance (1100 ℃ -water cooling), times1520

Application

Phosphate high alumina bricks are mainly used in dry process cement production kilns, rotary kilns, phosphorus chemical kilns, etc. Phosphate high alumina bricks have high refractoriness, good wear resistance and high strength.

评论

发表评论

此博客中的热门博文

High Alumina Anchor Bricks

图片
  High alumina anchor bricks are made of natural high-grade bauxite as the main refractory raw material, adding soft or semi-soft clay as a binder to the high-alumina clinker to start batching, mixing, molding, drying, and finally firing. Shaped high alumina refractory bricks. Characteristics High temperature volume stability. Good corrosion resistance. High softening temperature under load. Anti-peeling, high compressive strength. High Alumina Anchor Brick Specifications Item Al2O3 (%) ≥55 ≥60 ≥75 CaO (%) ≤2 ≤2 ≤2 Cold Crushing Strength, MPa ≥50 ≥50 ≥55 Tensile Strength, MPa ≥4 ≥4.1 ≥4.2 Refractoriness under load 0.2MPa, °C ≥1450 ≥1500 ≥1520 Apparent Porosity, % ≤22(24) ≤23(24) ≤21(23) Bulk Density, g/cm3 2.3 2.35-2.4 2.5-2.6 ting Permanent Linear Change (1500°Cx2h), % -0.4~+0.2 -0.3~+0.2 -0.3~+0.2 Application High-alumina anchor bricks are refractory bricks for the furnace roof and wall of the heating furnace, which can meet the needs of the lining of the heating furnace, ensure ...
阅读全文

High Alumina Checker Bricks

图片
  High alumina checker bricks have excellent thermal performance such as large heat storage area, smooth ventilation, and low resistance. It is also a heat transfer medium, mainly used for heat storage in the upper part of the regenerator of the hot blast stove. It plays an important role in the process of heating cold air into hot air. Features Has good volume stability. With high temperature load creep performance. High density, low porosity. High Alumina Checker Bricks Specifications Item RL-65 RL-55 RL-48 Al2O3 (%) ≥65 ≥55 ≥48 Refractoriness (℃) ≥1780 ≥1760 ≥1740 Refractoriness Under Load of 0.2MPa, ℃ ≥1500 ≥1470 ≥1420 Linear Change after Reheating, %, 1500℃x2h 0.1~-0.4 0.1~-0.4 0.1~-0.4 Apparent Porosity (%) 23 22 22 Cold Crushing Strength, MPa ≥50 ≥45 ≥40 Application It is mainly used for hot blast stoves. When the temperature is under 900℃, fire clay brick is used; while the temperature is higher than 900℃, the material of checker brick should be high alumina, mullite, silli...
阅读全文

Silicon Bricks For Glass Kiln

图片
  The SiO2 content of silica bricks for glass kilns is 96-98%. Its density is 2.35-2.38g/cm3. It has high structural strength at high temperature, such as high load softening temperature (1640~1700℃) and low creep rate. After absorbing a small amount of alkali components in addition to very slight fusion corrosion, and doesn’t reduce the structural strength of the kiln roof. Product characteristics of silica bricks for glass kiln High temperature volume stability. The glass liquid is slightly polluted. Chemical corrosion resistance. Small bulk density, which can reduce the weight of the furnace body. Silicon Bricks For Glass Kiln Specifications Item K BG-96 a K BG-96b K BG-9 5 SiO2 (%) ≥96 ≥96 ≥96 FeO3 (%) ≤0.6 ≤0.6 ≤0.6 Melting index, Al2O3+2R2O3 (%) ≤0.5 ≤0.7 – Apparent porosity (%) ≤21 ≤ 22 ≤ 22 True Density (g/cm3) ≤2.34 ≤2.34 ≤2.34 0.2MPa Load softening temperature (℃) ≥1680 ≥1670 ≥1670 N ormal temperature compressive strength (MPa) ≥40 ≥35 ≥ 30 re-burn line change. 1450℃*2h ...
阅读全文